2304 alloy steel
Utenti che stanno guardando questo topic:0 Registrati,0 Nascosti e 0 Ospiti
Utenti registrati: Nessuno


 
Nuovo Topic   Rispondi    Indice del forum -> Parole al Vento
PrecedenteInvia Email a un amico.Utenti che hanno visualizzato questo argomentoSalva questo topic come file txtVersione stampabileMessaggi PrivatiSuccessivo
Autore Messaggio
wangkiky








Registrato: 06/11/15 06:09
Messaggi: 1329
wangkiky is offline 

Localitą: shanghai,shanghai


Sito web: http://ecooutdoorfloor...

MessaggioInviato: Mar Ott 16, 2018 4:38 am    Oggetto:  2304 alloy steel
Descrizione:
Rispondi citando

The 304 alloy is duplex stainless steel consisting of 23% chromium and 4% nickel. The corrosion resistance of the 2304 alloy is similar to that of 316L. In addition, its mechanical property is that the yield strength is two times of the 304L/316L austenite grade. This feature allows the designer to reduce the weight of the product when designing the product, especially the pressure vessel.[url=https://www.steelsheetguide.com/stainless-supply/2241.html]Stainless Steel Welding Square Tube 304[/url]
This alloy is especially suitable for the temperature range of -50 degree C /+300 degree C (-58 F/572 F/572 F). In the case of strict restrictions (especially for welded structures), it can also be used for lower temperatures.
Compared with 304 and 316 austenite, 2304 alloy has stronger stress corrosion resistance because of its dual phase microstructure, lower nickel content and higher chromium content.
Stress corrosion resistance[url=https://www.steelsheetguide.com/stainless-steel/1264.html]Forging Steel Pipe Fittings[/url]
Stress corrosion tests in a solution of chloride concentration (8 ppm 02) PH=7, > 1000 h show that 2304 has higher stress corrosion resistance than 304L and 316L due to higher chromium content and lower nickel content.
This is a typical characteristic of duplex stainless steel. Under the same conditions, 2205 alloy is superior to 2304.
Other corrosion resistance[url=https://www.steelsheetguide.com/stainless-supply/1125.html]304 Stainless Steel Wire Rope 1x19 7x7 7x19[/url]
The 2304 alloy duplex stainless steel has passed most tests of standard IC, such as ASTM, A262E and C tests. Its corrosion rate in 65% boiling nitric acid is higher than that in 316L. Because of its high yield strength, the alloy is very suitable for corrosion and corrosion.
Torna in cima
Profilo Messaggio privato Invia email HomePage
Adv



MessaggioInviato: Mar Ott 16, 2018 4:38 am    Oggetto: Adv






Torna in cima
Mostra prima i messaggi di:   
Nuovo Topic   Rispondi    Indice del forum -> Parole al Vento Tutti i fusi orari sono GMT + 1 ore
Pagina 1 di 1

 
Vai a:  
Puoi inserire nuovi Topic in questo forum
Puoi rispondere ai Topic in questo forum
Non puoi modificare i tuoi messaggi in questo forum
Non puoi cancellare i tuoi messaggi in questo forum
Non puoi votare nei sondaggi in questo forum
Puoi allegare files in questo forum
Puoi scaricare files da questo forum





Udu Biologia Lecce topic RSS feed 
Powered by MasterTopForum.com with phpBB © 2003 - 2008